خوردگی حفره‌ای در جوش فلزات فولاد ضد زنگ سوپر دوبلکس

Effects of Heat Input on Pitting Corrosion in

Super Duplex Stainless Steel Weld Metals

اثر حرارت ورودی بر خوردگی حفره‌ای در جوش فلزات فولاد ضد زنگ سوپر دوبلکس

ABSTRACT

Due to the difference in reheating effects depending on the heat input of subsequent weld passes, the microstructure of the weld metal varies between acicular type austenite and a mixture of polygonal type and grain boundary mixed austenite. These microstructural changes may affect the corrosion properties of duplex stainless steel welds. This result indicates that the pitting resistance of the weld can be strongly influenced by the morphology of the secondary austenite phase. In particular, the ferrite phase adjacent to the acicular type austenite phase shows a lower Pitting Resistance Equivalent (PRE) value of 25.3, due to its lower chromium and molybdenum contents, whereas the secondary austenite phase maintains a higher PRE value of more than 38. Therefore, it can be inferred that the pitting corrosion is mainly due to the formation of ferrite phase with a much lower PRE value.

  

 

 جهت دانلود رایگان نسخه لاتین این مقاله اینجا کلیک کنید .

چکیده

با توجه به تفاوت در اثرات گرمایش مجدد بسته به حرارت ورودی پاسهای جوش متعاقب، ریزساختار فلز جوش بین آستنیت سوزنی و مخلوطی از آستنیت مخلوط چند ضلعی و مرز دانه متفاوت است. این تغییرات ریزساختاری ممکن است خواص خوردگی جوش فولاد ضدزنگ دوبلکس را تحت تاثیر قرار دهد. این نتیجه نشان می‌دهد که مقاومت حفره‌ای شدن جوش به شدت می تواند از سوی مورفولوژی فاز آستنیت ثانویه تحت تاثیر قرار گیرد. به ویژه، فاز فریت مجاور به فاز آستنیتی سوزنی با توجه به مقدار کروم و مولیبدن کمتر، یک مقدار مقاومت حفره‌ای شدن (PRE) پایین‌تری  برابر با 3/25 نشان می‌دهد، در حالیکه فاز آستنیت ثانویه مقدار PRE بالاتر از 38 را حفظ می‌کند. بنابراین، می توان نتیجه گرفت که به طور عمده خوردگی حفره‌ای به دلیل تشکیل فاز فریت با مقدار PRE خیلی پایین‌تر است.