Corrosion fatigue behaviour of aluminium alloy 6061-T651 welded

using fully automatic GMAW and ER5183 filler alloy

رفتار خستگی خوردگی آلیاژ آلومینیوم 6061-T651 جوش داده شده با (GMAW)

با آلیاژ ER5183 به عنوان فیلر

ABSTRACT

The fatigue life of aluminium 6061-T651 at various applied stress amplitudes in the unwelded and welded condition was found to be significantly reduced on immersion in a 3.5% NaCl simulated sea water solution, compared to that measured in ambient air. The ratio of fatigue life in NaCl test solution to that in air increased as the stress amplitude decreased. The observed reduction in the fatigue life in the NaCl test solution was most likely due to the presence of pits which nucleated on second phase particles or precipitates. Welded joints performed using pulsed gas metal arc welding and ER5183 filler wire failed at the interface between the weld metal and the heat-affected zone as a result of a high pitting rate in this region.


  

 

   جهت دانلود رایگان نسخه لاتین این مقاله اینجا کلیک کنید .


چکیده

مشاهده شد که عمر خستگی آلیاژ آلومینیوم 6061-T651 در دامنه تنش های به کار برده شده در شرایط جوشکاری شده و نشده پس از غوطه وری در محلول آب نمک 3.5 درصد (محلول شبیه ساز آب دریا) در مقایسه با هوای محیط به مقدار چشمگیری کاهش یافت. عمر خستگی در محلول آزمایش NaCl نسبت به هوا با کاهش دامنه تنش، افزایش یافت. کاهش مشاهده شده در عمر خستگی محلول تست آب نمک بیشتر به دلیل حضور حفراتی است که بر روی ذرات یا رسوبات فاز دوم جوانه می زند. اتصالات با استفاده از جوشکاری الکترود مصرفی محافظت شده با گاز جوشکاری شد و فیلر آلیاژ ER5183 نتوانست فصل مشترک بین فلز جوش و ناحیه متاثر از حرارت به دلیل نرخ بالای حفره دار شدن در این ناحیه، را پر کند.