اتصال Inconel 625 به UNS 32205 به روش جوشکاری پرتو الکترونی

Investigations on the structure – Property relationships of

electron beam welded Inconel 625 and UNS 32205

بررسی روابط خواص-ساختار اتصال Inconel 625 به UNS 32205

به روش جوشکاری پرتو الکترونی

ABSTRACT

The metallurgical and mechanical properties of electron beam welded Ni based superalloy Inconel 625 and UNS S32205 duplex stainless steel plates have been investigated in the present study. Interface microstructure studies divulged the absence of any grain coarsening effects or the formation of any secondary phases at the heat affected zone (HAZ) of the electron beam (EB) weldments. Tensile studies showed that the fracture occurred at the weld zone in all the trials and the average weld strength was reported to be 850 MPa. Segregation of Mo rich phases was witnessed at the inter-dendritic arms of the fusion zone. The study recommended the use of EB welding for joining these dissimilar metals by providing detailed structure – property relationships.

  

 

 جهت دانلود رایگان نسخه لاتین این مقاله اینجا کلیک کنید .

چکیده

در تحقیق حاضر، خواص متالورژیکی و مکانیکی جوش پرتو الکترونی صفحات سوپرآلیاژ پایه‌ نیکل Inconel 625 به فولاد زنگ‌نزن دوپلکس UNS S32205 بررسی شده است. مطالعات ریزساختاری در فصل‌مشترک، عدم وجود هرگونه اثرات درشت‌دانگی و عدم تشکیل هرگونه فاز ثانویه در ناحیه‌ی متاثر از حرارت (HAZ) را در جوش‌های پرتوی الکترونی (EB) نشان دادند. آزمون‌های کششی نشان دادند که در تمامی نمونه‌ها، شکست از ناحیه‌ی جوش رخ داد و استحکام متوسط جوش برابر 850 MPa گزارش شد. جدایش فازهای غنی از Mo در بازوهای درون-دندریتی در ناحیه‌ی ذوب مشاهده گشت. این تحقیق بر اساس جزئیات تهیه‌شده از روابط ساختار-خواص، استفاده از جوشکاری EB برای اتصال این فلزات غیرهمجنس را پیشنهاد می‌کند.